Flat Bar

The material is resistant to chloride ion corrosion so that the Stainless Steel 316 Flat Bar is used in marine applications with ease. It is also used in applications that need structural strength. The minimum tensile strength of the material is 515MPa and the minimum yield strength is 205MPa. The Polished Stainless Steel Flat Bar can also operate under high temperatures up to 870 degrees Celsius. The strength, corrosion resistance and the high temperature tolerance properties make the bars applied in ship building, marine, sea water, chemical, food processing and in boilers and heater applications. As a leading SS Flat Bar Manufacturer India, we provide solutions for all your needs.
Flat Bar Specification List
Grade All Grades
Bar Finishing Bright, Polish & Flat
Otder Services Machining (CNC), Centreless Grinding (CG), Heat Treatment, Anneling, Pickling, Polish, Rolling, Forging, Cutting, Bending, Minor Fabrication,
Test Certificate Manufacturer Test Certificate / Laboratory Test Certificate from Govt. Approved Lab / Under tdird Party Inspection & witd Excise Gate Pass to avail Modvat benefit.
Stainless Steel 304 Flat Bar Weight
FlatS
Size(mm) WT PER FEET IN KGS WT PER MTR IN KGS
16 0.62 2.05
18 0.79 2.59
20 0.76 2.49
22 1.18 3.87
25 1.52 5.00
28 1.91 6.27
30 2.19 7.20
32 2.50 8.19
36 3.16 10.37
38 3.52 11.55
40 3.90 12.80
45 4.94 16.20
50 6.10 20.00
56 7.65 25.08
60 - -
65 - -
70 - -
75 - -
80 - -
90 - -
100 - -
Processing Steps for SS Flat Bar
  • Stainless Steel Flat Bar Cutting
  • Stainless Steel 304 Flat Bar Heat Treating
  • Stainless Steel 316 Flat Bar Machining
  • SS Flat Bar Additional Services
Chemical Composition
Element C Cr Mn Ni P S Si
SS 304 8.0 – 11.0 18.0 – 20.0 2.0 max 8.0 – 11.0 0.045 max 0.03 max 1.0 max
SS 304L 8.0 – 11.0 18.0 – 20.0 2.0 max 8.0 – 12.0 0.045 max 0.03 max 1.0 max
SS 316 0.08 18.0 2.00 14.0 0.045 max 0.03 max 0.75 max
SS 316L 0.08 18.0 2.00 14.0 0.045 max 3.00 max 0.10 max
Mechanical Properties Analysis
Element Tensile Strength Yield Strength Elongation Reduction in Area Hardness
SS 304 Psi – 85,000 Psi – 45,000 50% 55% Rb 180